Multi-piece integrated core-shell structure for making cast component

ABSTRACT

The present disclosure generally relates to partial integrated core-shell investment casting molds that can be assembled into complete molds. Each section of the partial mold may contain both a portion of a core and portion of a shell. Each section can then be assembled into a mold for casting of a metal part. The partial integrated core-shell investment casting molds and the complete molds may be provided with filament structures corresponding to cooling hole patterns on the surface of the turbine blade or the stator vane, which provides a leaching pathway for the core portion after metal casting. The invention also relates to core filaments that can be used to supplement the leaching pathway, for example in a core tip portion of the mold.

INTRODUCTION

The present disclosure generally relates to graded investment casting two piece core-shell mold components and processes utilizing these components. The two piece core-shell mold is assembled from a partial mold including a first core and shell portion. The two piece core-shell mold is assembled by attaching the first core and shell portion to at least a second core and shell portion of a second partial mold. The two piece core-shell mold made in accordance with the present invention may also include integrated ceramic filaments between the core and shell of the mold that can be utilized to form holes, i.e., effusion cooling holes, in the cast component made from these two-piece molds. The use of sufficient ceramic filaments between core and shell to both locate and provide leaching pathways for the core serpentine also enables the elimination of ball braze chutes. Ceramic filaments between the tip plenum core and the shell may also be provided to support a floating tip plenum, eliminating the need for traditional tip pins, and their subsequent closure by brazing. The integrated core-shell molds provide useful properties in casting operations, such as in the casting of superalloys used to make turbine blades and stator vanes for jet aircraft engines or power generation turbine components.

BACKGROUND

Many modern engines and next generation turbine engines require components and parts having intricate and complex geometries, which require new types of materials and manufacturing techniques. Conventional techniques for manufacturing engine parts and components involve the laborious process of investment or lost-wax casting. One example of investment casting involves the manufacture of a typical rotor blade used in a gas turbine engine. A turbine blade typically includes hollow airfoils that have radial channels extending along the span of a blade having at least one or more inlets for receiving pressurized cooling air during operation in the engine. The various cooling passages in a blade typically include a serpentine channel disposed in the middle of the airfoil between the leading and trailing edges. The airfoil typically includes inlets extending through the blade for receiving pressurized cooling air, which include local features such as short turbulator ribs or pins for increasing the heat transfer between the heated sidewalls of the airfoil and the internal cooling air.

The manufacture of these turbine blades, typically from high strength, superalloy metal materials, involves numerous steps shown in FIG. 1. First, a precision ceramic core is manufactured to conform to the intricate cooling passages desired inside the turbine blade. A precision die or mold is also created which defines the precise 3-D external surface of the turbine blade including its airfoil, platform, and integral dovetail. A schematic view of such a mold structure is shown in FIG. 2. The ceramic core 200 is assembled inside two die halves which form a space or void therebetween that defines the resulting metal portions of the blade. Wax is injected into the assembled dies to fill the void and surround the ceramic core encapsulated therein. The two die halves are split apart and removed from the molded wax. The molded wax has the precise configuration of the desired blade and is then coated with a ceramic material to form a surrounding ceramic shell. Then, the wax is melted and removed from the shell 202 leaving a corresponding void or space 201 between the ceramic shell 202 and the internal ceramic core 200 and tip plenum 204. Molten superalloy metal is then poured into the shell to fill the void therein and again encapsulate the ceramic core 200 and tip plenum 204 contained in the shell 202. The molten metal is cooled and solidifies, and then the external shell 202 and internal core 200 and tip plenum 204 are suitably removed leaving behind the desired metallic turbine blade in which the internal cooling passages are found. In order to provide a pathway for removing ceramic core material via a leaching process, a ball chute 203 and tip pins 205 are provided, which upon leaching form a ball chute and tip holes within the turbine blade that must subsequently be brazed shut.

The cast turbine blade may then undergo additional post-casting modifications, such as but not limited to drilling of suitable rows of film cooling holes through the sidewalls of the airfoil as desired for providing outlets for the internally channeled cooling air which then forms a protective cooling air film or blanket over the external surface of the airfoil during operation in the gas turbine engine. After the turbine blade is removed from the ceramic mold, the ball chute 203 of the ceramic core 200 forms a passageway that is later welded shut to provide the desired pathway of air through the internal voids of the cast turbine blade. However, these post-casting modifications are limited and given the ever increasing complexity of turbine engines and the recognized efficiencies of certain cooling circuits inside turbine blades, more complicated and intricate internal geometries are required. While investment casting is capable of manufacturing these parts, positional precision and intricate internal geometries become more complex to manufacture using these conventional manufacturing processes. Accordingly, it is desired to provide an improved casting method for three dimensional components having intricate internal voids.

Methods for using 3-D printing to produce a ceramic core-shell mold are described in U.S. Pat. No. 8,851,151 assigned to Rolls-Royce Corporation. The methods for making the molds include powder bed ceramic processes such as disclosed U.S. Pat. No. 5,387,380 assigned to Massachusetts Institute of Technology, and selective laser activation (SLA) such as disclosed in U.S. Pat. No. 5,256,340 assigned to 3D Systems, Inc. The ceramic core-shell molds according to the '151 patent are limited by the printing resolution capabilities of these processes. As shown in FIG. 3, the core portion 301 and shell portion 302 of the integrated core-shell mold is held together via a series of tie structures 303 provided at the bottom edge of the mold. Cooling passages are proposed in the '151 patent that include staggered vertical cavities joined by short cylinders, the length of which is nearly the same as its diameter. A superalloy turbine blade is then formed in the core-shell mold using known techniques disclosed in the '151 patent, and incorporated herein by reference. After a turbine blade is cast in one of these core-shell molds, the mold is removed to reveal a cast superalloy turbine blade.

There remains a need to prepare ceramic core-shell molds produced using higher resolution methods that are capable of providing fine detail cast features in the end-product of the casting process.

SUMMARY

The present invention relates to a novel casting mold that is formed as a two piece core-shell mold consisting of a first ceramic mold portion comprising a first shell portion and optionally a first core portion and a second ceramic mold portion comprising a second shell portion and optionally a second shell portion, the first ceramic mold portion being adapted to interface with the second ceramic mold portion to form a two piece ceramic mold comprising a cavity between the first and/or second core portions and the first and second shell portions, the cavity adapted to define a cast component upon casting and removal of the ceramic mold. The first and/or second ceramic mold portion may be provided with at least one attachment point to facilitate assembly into a complete core-shell mold. Non-limiting examples of suitable attachment points include, for example, an interlocking arrangement, such as for example a tongue and groove or dovetail type attachment. Another non-limiting example of a suitable attachment point is a rabbet joint.

In one embodiment, the invention relates to a method of making a first partial ceramic mold having a core, a shell, and a locking feature. The method having steps of (a) contacting a cured portion of a workpiece with a liquid ceramic photopolymer; (b) irradiating a portion of the liquid ceramic photopolymer adjacent to the cured portion through a window contacting the liquid ceramic photopolymer; (c) removing the workpiece from the uncured liquid ceramic photopolymer; and (d) repeating steps (a)-(c) until a first partial ceramic mold is formed, the first partial ceramic mold comprising a core portion, a shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of one side of a cast component upon casting and removal of the first partial ceramic mold, and at least one locking feature. After step (d), the process may further include steps for making a cast component, for example by (e) repeating steps (a) through (d) to make a second partial ceramic mold having a shell and a locking feature; (f) forming a two piece ceramic mold having a core and shell by interfacing the first partial ceramic mold with the second partial ceramic mold via their locking features; (g) pouring a liquid metal into the two piece ceramic casting mold and solidifying the liquid metal to form the cast component. After step (g), the process may further include a step (h) comprising removing the mold from the cast component, and this step preferably involves mechanically or physically detaching the first ceramic mold portion from the second ceramic mold portion, and optionally also by chemical leaching in an alkaline bath. The step of removing the mold from the cast component can also include leaching at least a portion of the ceramic core through the holes in the cast component provided by the filaments.

In another embodiment, the invention relates to a method of making a two piece ceramic mold having a core and shell, the two piece ceramic mold being formed from a first ceramic mold portion and a second ceramic mold portion. The method having steps of (a) contacting a cured portion of a first workpiece with a liquid ceramic photopolymer; (b) irradiating a portion of the liquid ceramic photopolymer adjacent to the cured portion through a window contacting the liquid ceramic photopolymer; (c) removing the workpiece from the uncured liquid ceramic photopolymer; and (d) repeating steps (a)-(c) until a first ceramic mold portion is formed, the first ceramic mold comprising at least one locking feature, optionally a first core portion, a first shell portion, and if the first ceramic mold portion is formed with a first core portion, then the first shell portion has at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of a first side of a cast component upon casting and removal of the ceramic mold; (e) repeating steps (a)-(d) with a second workpiece until a second ceramic mold portion is formed, the second ceramic mold portion comprising at least one locking feature, optionally a second core portion, a second shell portion, and if the second ceramic mold portion is formed with a second core portion, then the second shell portion has at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of a second side of a cast component upon casting and removal of the two piece ceramic mold; (f) attaching the first ceramic mold portion to the second ceramic mold portion via their locking features to form a two piece ceramic mold having a core and shell. After step (f), the process may further include a step (g) of pouring a liquid metal into a two piece casting mold and solidifying the liquid metal to form the cast component. After step (g), the process may further include a step (h) comprising removing the two piece mold from the cast component, and this step preferably involves mechanically or physically detaching the first ceramic mold portion from the second ceramic mold portion, and optionally also chemical leaching in an alkaline bath. The step of removing the mold from the cast component can also include leaching at least a portion of the ceramic core through the holes in the cast component provided by the filaments.

In another aspect, the invention relates to a method of preparing a cast component. The method includes steps of pouring a liquid metal into a two piece ceramic casting mold and solidifying the liquid metal to form the cast component, the two piece ceramic casting mold comprising a first ceramic mold portion, a second ceramic mold portion, a core portion, and at least one shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of the cast component upon casting and removal of the two piece ceramic mold, and one or both of the ceramic casting mold portions further comprising a plurality of filaments joining the core portion and the shell portion where each filament spans between the core and shell, the filaments adapted to define a plurality of holes in the cast component upon removal of the two piece mold, and each ceramic mold portion further comprising at least one attachment point; and removing the two piece ceramic casting mold from the cast component by detaching the first ceramic mold portion from the second ceramic mold portion via their attachment points.

In another aspect, the invention relates to a method of preparing a cast component. The method includes steps of assembling a first core portion and a first shell portion of a two piece ceramic mold with at least a second core portion and second shell portion to form a two piece ceramic mold comprising a cavity between the first and second core portions and the first and second shell portions, the cavity adapted to define the shape of the cast component upon casting and removal of the two piece ceramic mold, pouring a liquid metal into a two piece ceramic casting mold and solidifying the liquid metal to form the cast component, the two piece ceramic casting mold comprising a first ceramic mold portion, a second ceramic mold portion, a core portion, and at least one shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of the cast component upon casting and removal of the two piece ceramic mold, and one or both of the ceramic casting mold portions further comprising a plurality of filaments joining the core portion and the shell portion where each filament spans between the core and shell, the filaments adapted to define a plurality of holes in the cast component upon removal of the two piece mold, and each ceramic mold portion further comprising at least one attachment point; and removing the two piece ceramic casting mold from the cast component by detaching the first ceramic mold portion from the second ceramic mold portion via their attachment points.

In one aspect, the cast component is a turbine blade or a stator vane. Preferably the turbine blade or stator vane is used in a gas turbine engine in, for example, an aircraft engine or power generation. The turbine blade or stator vane is preferably a single crystal cast turbine blade having a cooling hole pattern defined by the ceramic filaments mentioned above. Preferably, the filaments join the core portion and shell portion where each filament spans between the core and shell, the filaments having a cross sectional area ranging from 0.1 to 2 mm².

The large number of filaments used to form a cooling hole pattern may provide sufficient strength to support the tip core. If the tip filaments are made to support tip plenum core, they may be made larger, i.e., >2 mm cross section area, and a much lower number of filaments, or a single filament, could be used. Although two to four of these larger filaments is a desirable number. After casting, any holes or notches remaining in the tip plenum sidewalls as a result of the filaments may be brazed shut or incorporated into the turbine blade or stator vane design, or the filaments may be placed outside the finish machined shape of the component to prevent the need for this.

In another aspect, the invention relates to a two piece ceramic casting mold comprising a first ceramic casting mold portion and a second ceramic casting mold portion, each ceramic casting mold portion having a core portion and a shell portion with at least one cavity between the core portion and the shell portion, the cavity adapted to define the shape of one side of the cast component upon casting and removal of the two piece ceramic mold; a plurality of filaments joining the core portion and the shell portion where each filament spans between the core and shell, the filaments adapted to define a plurality of holes providing fluid communication between a cavity within the cast component defined by the core portion and an outer surface of the cast component upon removal of the two piece mold. Preferably, the cast component is a turbine blade or stator vane and the plurality of filaments joining the core portion and shell portion define a plurality of cooling holes in the turbine blade upon removal of the two piece mold. Preferably, the plurality of filaments joining the core portion and shell portion have a cross sectional area ranging from 0.01 to 2 mm². The ceramic may be a photopolymerized ceramic or a cured photopolymerized ceramic.

In one aspect, the first core portion and/or the first shell portion includes at least one interlocking feature adapted to interface with an interlocking feature on the second core portion and/or second shell portion. Preferably the interlocking feature is an interlocking tongue or groove, an interlocking dovetail or a rabbet joint with an interlocking peg, adapted to fasten with a second partial ceramic casting mold.

In one aspect, the first core portion and/or first shell portion comprises a pin support or bumper facing the first core portion or the first shell portion.

In one aspect, ceramic mold comprises a plurality of tie structures joining the core portion and shell portion, the tie structures adapted to define a plurality of holes in the cast component upon removal of the mold.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flow diagram showing the steps for conventional investment casting.

FIG. 2 is a schematic diagram showing an example of a conventional scheme for a core-shell mold with ball chute prepared by a conventional process.

FIG. 3 shows a perspective view of a prior art integrated core-shell mold with ties connecting the core and shell portions.

FIGS. 4, 5, 6 and 7 show schematic lateral sectional views of a device for carrying out successive phases of the method sequence for direct light processing (DLP)

FIG. 8 shows a schematic sectional view along the line A-A of FIG. 7.

FIG. 9 shows a side view of two core-shell subassemblies and the direction of attachment in accordance with an embodiment of the invention.

FIG. 10 shows an assembled view of the two core-shell subassemblies shown in FIG. 9.

FIG. 11 shows a two part integral core-shell mold with attachment points that may be mechanically interlocked.

FIG. 12 shows an interlocking tongue and groove that can be used to attach two core-shell subassemblies in accordance with an embodiment of the invention.

FIG. 13 shows an interlocking dovetail that can be used to attach two core-shell subassemblies in accordance with an embodiment of the invention.

FIG. 14 shows a rabbet joint with integral interlocking peg that can be used to attach two core-shell subassemblies in accordance with an embodiment of the invention.

FIG. 15 shows a two-part integral core-shell mold including filaments extending from the core to the shell for purposes of providing cooling holes in the surface of a turbine blade in accordance with an embodiment of the invention.

FIG. 16 shows a two-part integral core-shell mold including filaments extending from the core to the shell for purposes of providing cooling holes in the surface of a turbine blade in accordance with an embodiment of the invention.

FIG. 17 is a schematic view of an integrated core shell mold having core print filaments exiting beside a blade tip in accordance with an embodiment of the invention.

DETAILED DESCRIPTION

The detailed description set forth below in connection with the appended drawings is intended as a description of various configurations and is not intended to represent the only configurations in which the concepts described herein may be practiced. The detailed description includes specific details for the purpose of providing a thorough understanding of various concepts. However, it will be apparent to those skilled in the art that these concepts may be practiced without these specific details. For example, the present invention provides a preferred method for making cast metal parts, and preferably those cast metal parts used in the manufacture of j et aircraft engines. Specifically, the production of single crystal, nickel-based superalloy cast parts such as turbine blades, vanes, and shroud components can be advantageously produced in accordance with this invention. However, other cast metal components may be prepared using the techniques and integrated ceramic molds of the present invention.

The present inventors recognized that prior processes known for making integrated core-shell molds lacked the fine resolution capability necessary to print filaments extending between the core and shell portion of the mold of sufficiently small size and quantity to result in effusion cooling holes in the finished turbine blade. In the case of earlier powder bed processes, such as disclosed in U.S. Pat. No. 5,387,380 assigned to Massachusetts Institute of Technology, the action of the powder bed recoater arm precludes formation of sufficiently fine filaments extending between the core and shell to provide an effusion cooling hole pattern in the cast part. Other known techniques such as selective laser activation (SLA) such as disclosed in U.S. Pat. No. 5,256,340 assigned to 3D Systems, Inc. that employ a top-down irradiation technique may be utilized in producing an integrated core-shell mold in accordance with the present invention. However, the available printing resolution of these systems significantly limits the ability to make filaments of sufficiently small size to serve as effective cooling holes in the cast final product.

The present inventors have found that the integrated core-shell mold of the present invention can be manufactured using direct light processing (DLP). DLP differs from the above discussed powder bed and SLA processes in that the light curing of the polymer occurs through a window at the bottom of a resin tank that projects light upon a build platform that is raised as the process is conducted. With DLP an entire layer of cured polymer is produced simultaneously, and the need to scan a pattern using a laser is eliminated. Further, the polymerization occurs between the underlying window and the last cured layer of the object being built. The underlying window provides support allowing thin filaments of material to be produced without the need for a separate support structure. In other words, producing a thin filament of material bridging two portions of the build object is difficult and was typically avoided in the prior art. For example, the '151 patent discussed above in the background section of this application used vertical plate structures connected with short cylinders, the length of which was on the order of their diameter. Staggered vertical cavities are necessitated by the fact that the powder bed and SLA techniques disclosed in the '151 patent require vertically supported ceramic structures and the techniques are incapable of reliably producing filaments. In addition, the available resolution within a powder bed is on the order of ⅛″ making the production of traditional cooling holes impracticable. For example, round cooling holes generally have a diameter of less than 2 mm corresponding to a cooling hole area below 3.2 mm². Production of a hole of such dimensions requires a resolution far below the size of the actual hole given the need to produce the hole from several voxels. This resolution is simply not available in a powder bed process. Similarly, stereolithography is limited in its ability to produce such filaments due to lack of support and resolution problems associated with laser scattering. But the fact that DLP exposes the entire length of the filament and supports it between the window and the build plate enables producing sufficiently thin filaments spanning the entire length between the core and shell to form a ceramic object having the desired cooling hole pattern. Although powder bed and SLA may be used to produce filaments, their ability to produce sufficiently fine filaments as discussed above is limited.

One suitable DLP process is disclosed in U.S. Pat. No. 9,079,357 assigned to Ivoclar Vivadent AG and Technische Universitat Wien, as well as WO 2010/045950 A1 and US 2011310370, each of which are hereby incorporated by reference and discussed below with reference to FIGS. 4-8. The apparatus includes a tank 404 having at least one translucent bottom portion 406 covering at least a portion of the exposure unit 410. The exposure unit 410 comprises a light source and modulator with which the intensity can be adjusted position-selectively under the control of a control unit, in order to produce an exposure field on the tank bottom 406 with the geometry desired for the layer currently to be formed. As an alternative, a laser may be used in the exposure unit, the light beam of which successively scans the exposure field with the desired intensity pattern by means of a mobile mirror, which is controlled by a control unit.

Opposite the exposure unit 410, a production platform 412 is provided above the tank 404; it is supported by a lifting mechanism (not shown) so that it is held in a height-adjustable way over the tank bottom 406 in the region above the exposure unit 410. The production platform 412 may likewise be transparent or translucent in order that light can be shone in by a further exposure unit above the production platform in such a way that, at least when forming the first layer on the lower side of the production platform 412, it can also be exposed from above so that the layer cured first on the production platform adheres thereto with even greater reliability.

The tank 404 contains a filling of highly viscous photopolymerizable material 420. The material level of the filling is much higher than the thickness of the layers which are intended to be defined for position-selective exposure. In order to define a layer of photopolymerizable material, the following procedure is adopted. The production platform 412 is lowered by the lifting mechanism in a controlled way so that (before the first exposure step) its lower side is immersed in the filling of photopolymerizable material 420 and approaches the tank bottom 406 to such an extent that precisely the desired layer thickness A (see FIG. 5) remains between the lower side of the production platform 412 and the tank bottom 406. During this immersion process, photopolymerizable material is displaced from the gap between the lower side of the production platform 412 and the tank bottom 406. After the layer thickness A has been set, the desired position-selective layer exposure is carried out for this layer, in order to cure it in the desired shape. Particularly when forming the first layer, exposure from above may also take place through the transparent or translucent production platform 412, so that reliable and complete curing takes place particularly in the contact region between the lower side of the production platform 412 and the photopolymerizable material, and therefore good adhesion of the first layer to the production platform 412 is ensured. After the layer has been formed, the production platform is raised again by means of the lifting mechanism.

These steps are subsequently repeated several times, the distance from the lower side of the layer 422 formed last to the tank bottom 406 respectively being set to the desired layer thickness A and the next layer thereupon being cured position-selectively in the desired way.

After the production platform 412 has been raised following an exposure step, there is a material deficit in the exposed region as indicated in FIG. 6. This is because after curing the layer set with the thickness A, the material of this layer is cured and raised with the production platform and the part of the shaped body already formed thereon. The photopolymerizable material therefore missing between the lower side of the already formed shaped body part and the tank bottom 406 must be filled from the filling of photopolymerizable material 420 from the region surrounding the exposed region. Owing to the high viscosity of the material, however, it does not flow by itself back into the exposed region between the lower side of the shaped body part and the tank bottom, so that material depressions or “holes” can remain here.

In order to replenish the exposure region with photopolymerizable material, an elongate mixing element 432 is moved through the filling of photopolymerizable material 420 in the tank. In the exemplary embodiment represented in FIGS. 4 to 8, the mixing element 432 comprises an elongate wire which is tensioned between two support arms 430 mounted movably on the side walls of the tank 404. The support arms 430 may be mounted movably in guide slots 434 in the side walls of the tank 404, so that the wire 432 tensioned between the support arms 430 can be moved relative to the tank 404, parallel to the tank bottom 406, by moving the support arms 430 in the guide slots 434. The elongate mixing element 432 has dimensions, and its movement is guided relative to the tank bottom, such that the upper edge of the elongate mixing element 432 remains below the material level of the filling of photopolymerizable material 420 in the tank outside the exposed region. As can be seen in the sectional view of FIG. 8, the mixing element 432 is below the material level in the tank over the entire length of the wire, and only the support arms 430 protrude beyond the material level in the tank. The effect of arranging the elongate mixing element below the material level in the tank 404 is not that the elongate mixing element 432 substantially moves material in front of it during its movement relative to the tank through the exposed region, but rather this material flows over the mixing element 432 while executing a slight upward movement. The movement of the mixing element 432 from the position shown in FIG. 6, to, for example, a new position in the direction indicated by the arrow A, is shown in FIG. 7. It has been found that by this type of action on the photopolymerizable material in the tank, the material is effectively stimulated to flow back into the material-depleted exposed region between the production platform 412 and the exposure unit 410.

The movement of the elongate mixing element 432 relative to the tank may firstly, with a stationary tank 404, be carried out by a linear drive which moves the support arms 430 along the guide slots 434 in order to achieve the desired movement of the elongate mixing element 432 through the exposed region between the production platform 412 and the exposure unit 410. As shown in FIG. 8, the tank bottom 406 has recesses 406′ on both sides. The support arms 430 project with their lower ends into these recesses 406′. This makes it possible for the elongate mixing element 432 to be held at the height of the tank bottom 406, without interfering with the movement of the lower ends of the support arms 430 through the tank bottom 406.

Other alternative methods of DLP may be used to prepare the integrated two piece core-shell molds of the present invention. For example, the tank may be positioned on a rotatable platform. When the workpiece is withdrawn from the viscous platform between successive build steps, the tank may be rotated relative to the platform and light source to provide a fresh layer of viscous polymer in which to dip the build platform for building successive layers.

FIG. 9 shows a schematic side view of a two piece integrated core-shell mold 900 in accordance with an aspect of the invention. The first piece includes a partial core 901 and partial shell 902, and the second piece includes a partial core 903 and partial shell 904. The partial core 901 and partial shell 902 may be formed as one integral piece, or may be separate assemblies. The partial core-shell structures are provided with attachment points 905, 906, 907, and 908 that facilitate assembly into a complete core-shell mold 1000 as shown in FIG. 10. The two-piece molds of the present invention have the advantage that they can be inspected prior to assembly and casting. Previous integral one-piece molds had the disadvantage that due to the 3-D printed nature of the mold, inspection of the mold before casting was difficult.

As shown in FIG. 10, the core-shell mold 1000 may include structures integrally formed with the core 1001 or shell 1002 portion. For example, a core bumper 1003 may be provided, or a shell bumper 1004 may be provided. Upon assembly of the two-part mold, the bumpers 1003/1004 function to provide the required spacing between the core 1001 and shell 1002. A pin support 1005 may be provided integral to the shell, which abuts the core portion upon assembly of the two-part core-shell. Although not shown, a pin structure may be provided integral to the core.

FIG. 11 shows a two-part core shell mold 1100 having a first core/shell portion 1101/1102 and a second core-shell portion 1103/1104. In this embodiment, a first point of attachment 1105 is provided within the tip portion of the core assembly and a second point of attachment 1106 is provided at a portion of the shell region distal the core tip region. FIGS. 12-14 illustrate several non-limiting examples of attachment mechanisms provided in the ceramic core/shell assembly. FIG. 12 illustrates an interlocking tongue and groove type attachment 1200 with a first outside portion 1201, first inside portion 1202, second outside portion 1203, and second inside portion 1204. FIG. 13 illustrates an interlocking dovetail type attachment 1300 with a first outside portion 1301, first inside portion 1302, second outside portion 1303, and second inside portion 1304. FIG. 14 illustrates a rabbet joint with interlocking peg having a first outside portion 1401, first inside portion 1402, second outside portion 1403, and second inside portion 1404.

FIG. 15 shows an example of a two-part core-shell assembly 1500 having a first core portion 1501 with attachment mechanisms 1507, 1508 and a first shell portion 1502 with attachment mechanism 1511, a second core portion 1503 with attachment mechanisms 1509, 1510 and a second shell portion 1504 with attachment mechanism 1512. The first core portion 1501 and first shell portion 1502 are linked together with filaments 1505. The second core portion 1503 and second shell portion 1503 are linked together with filaments 1506. After casting of the metal within the core-shell mold and leaching of the filaments, the filaments define a cooling hole pattern in the cast turbine blade. As described in co-pending application, GE Docket #285020, these structures are preferably formed using the DLP process described in connection with FIGS. 4-11 above. By printing the ceramic mold using the above DLP printing process, the mold can be made in a way that allows the point of connections between the core and shell to be provided through filaments 1505 and/or 1506. Once the core-shell mold is printed, it may be subject to a post-heat treatment step to cure the printed ceramic polymer material. The cured ceramic mold may then be used similar to the traditional casting process used in the production of superalloy turbine blades. Notably because the filaments 1505 and 1506 are provided in a large quantity consistent with formation of a pattern of effusion cooling holes in the surface of a turbine blade, the need for a ball chute structure as shown in FIG. 2 may be eliminated.

The filaments 1505 and 1506 are preferably cylindrical or oval shape but may be curved or non-linear. Their exact dimensions may be varied according to a desired film cooling scheme for a particular cast metal part. For example cooling holes may have a cross sectional area ranging from 0.01 to 2 mm². In a turbine blade, the cross sectional area may range from 0.01 to 0.15 mm², more preferably from 0.05 to 0.1 mm², and most preferably about 0.07 mm². In the case of a vane, the cooling holes may have a cross sectional area ranging from 0.05 to 0.2 mm², more preferably 0.1 to 0.18 mm², and most preferably about 0.16 mm². The spacing of the cooling holes is typically a multiple of the diameter of the cooling holes ranging from 2× to 10× the diameter of the cooling holes, most preferably about 4-7× the diameter of the cooling holes.

The length of the filament 1505 and/or 1506 is dictated by the thickness of the cast component, e.g., turbine blade or stator vane wall thickness, and the angle at which the cooling hole is disposed relative to the surface of the cast component. The typical lengths range from 0.5 to 5 mm, more preferably between 0.7 to 1 mm, and most preferably about 0.9 mm. The angle at which a cooling hole is disposed is approximately 5 to 35° relative to the surface, more preferably between 10 to 20°, and most preferably approximately 12°. It should be appreciated that the methods of casting according to the present invention allow for formation of cooling holes having a lower angle relative to the surface of the cast component than currently available using conventional machining techniques.

FIG. 16 shows a side view of an integrated core-shell mold 1600 according to an embodiment of the present invention. As with the schematic shown in FIG. 15, the first core portion 1601 is connected to the first shell portion 1602 through several filaments 1605. Likewise, the second core portion 1603 is connected to the second shell portion 1604 through several filaments 1606. The first core portion 1601 and the first shell portion 1602 can be attached to the second core portion 1602 and the second shell portion 1604 via attachment mechanisms 1608, 1609, 1610 and 1611 to form the complete core-shell mold assembly 1600. The assembled core-shell mold 1600 defines a cavity 1607 for investment casting a turbine blade. FIG. 17 shows the cavity 1607 filled with a metal 1700, such as a nickel based alloy, i.e., Inconel. Upon leaching of the ceramic core-shell, the resulting cast object is a turbine blade or stator vane having a cooling hole pattern in the surface of the blade or vane. It should be appreciated that although FIGS. 16-17 provide a cross sectional view showing cooling holes at the leading and trailing edge of the turbine blade, that additional cooling holes may be provided where desired including on the sides of the turbine blades or any other location desired. In particular, the present invention may be used to form cooling holes within the casting process in any particular design. In other words, one would be able to produce conventional cooling holes in any pattern where drilling was used previously to form the cooling holes. However, the present invention will allow for cooling hole patterns previously unattainable due to the limitations of conventional technologies for creating cooling holes within cast components, i.e., drilling.

After leaching, the resulting holes in the turbine blade or stator vane from the core print filaments may be brazed shut if desired. Otherwise the holes left by the core print filaments may be incorporated into the design of the internal cooling passages. Alternatively, cooling hole filaments may be provided to connect the tip plenum core to the shell in a sufficient quantity to hold the tip plenum core in place during the metal casting step.

After printing the core-shell mold structures in accordance with the invention, the core-shell mold may be cured and/or fired depending upon the requirements of the ceramic core photopolymer material. Molten metal may be poured into the mold to form a cast object in the shape and having the features provided by the integrated core-shell mold. In the case of a turbine blade or a stator vane, the molten metal is preferably a superalloy metal that formed into a single crystal superalloy turbine blade or stator vane using techniques known to be used with conventional investment casting molds.

In an aspect, the present invention relates to the core-shell mold structures of the present invention incorporated or combined with features of other core-shell molds produced in a similar manner. The following patent applications include disclosure of these various aspects and their use:

U.S. patent application Ser. No. ______, titled “INTEGRATED CASTING CORE-SHELL STRUCTURE” with attorney docket number 037216.00036/284976, and filed Dec. 13, 2016;

U.S. patent application Ser. No. ______, titled “INTEGRATED CASTING CORE-SHELL STRUCTURE WITH FLOATING TIP PLENUM” with attorney docket number 037216.00037/284997, and filed Dec. 13, 2016;

U.S. patent application Ser. No. ______, titled “MULTI-PIECE INTEGRATED CORE-SHELL STRUCTURE WITH STANDOFF AND/OR BUMPER FOR MAKING CAST COMPONENT” with attorney docket number 037216.00042/284909A, and filed Dec. 13, 2016;

U.S. patent application Ser. No. ______, titled “INTEGRATED CASTING CORE SHELL STRUCTURE WITH PRINTED TUBES FOR MAKING CAST COMPONENT” with attorney docket number 037216.00032/284917, and filed Dec. 13, 2016;

U.S. patent application Ser. No. ______, titled “INTEGRATED CASTING CORE-SHELL STRUCTURE AND FILTER FOR MAKING CAST COMPONENT” with attorney docket number 037216.00039/285021, and filed Dec. 13, 2016;

U.S. patent application Ser. No. ______, titled “INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH NON-LINEAR HOLES” with attorney docket number 037216.00041/285064, and filed Dec. 13, 2016;

U.S. patent application Ser. No. ______, titled “INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT WITH COOLING HOLES IN INACCESSIBLE LOCATIONS” with attorney docket number 037216.00055/285064A, and filed Dec. 13, 2016;

U.S. patent application Ser. No. ______, titled “INTEGRATED CASTING CORE SHELL STRUCTURE FOR MAKING CAST COMPONENT HAVING THIN ROOT COMPONENTS” with attorney docket number 037216.00053/285064B, and filed Dec. 13, 2016.

The disclosures of each of these applications are incorporated herein in their entirety to the extent they disclose additional aspects of core-shell molds and methods of making that can be used in conjunction with the core-shell molds disclosed herein.

This written description uses examples to disclose the invention, including the preferred embodiments, and also to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal language of the claims. Aspects from the various embodiments described, as well as other known equivalents for each such aspect, can be mixed and matched by one of ordinary skill in the art to construct additional embodiments and techniques in accordance with principles of this application. 

1. A partial ceramic casting mold comprising: a first core portion and a first shell portion, the first core portion and first shell portion adapted to interface with at least a second core portion and second shell portion to form a ceramic mold comprising a cavity between the first and second core portions and the first and second shell portions, the cavity adapted to define a cast component upon casting and removal of the ceramic mold.
 2. The partial ceramic casting mold of claim 1, wherein the cast component is a turbine blade or a stator vane.
 3. The partial ceramic casting mold of claim 1, wherein the first core portion or the first shell portion includes at least one interlocking feature adapted to interface with an interlocking feature on the second core portion or second shell portion.
 4. The partial ceramic casting mold of claim 3, wherein the interlocking feature is an interlocking tongue or groove adapted to fasten with a second partial ceramic casting mold.
 5. The partial ceramic casting mold of claim 3, wherein the interlocking feature is an interlocking dovetail adapted to fasten with a second partial ceramic casting mold.
 6. The partial ceramic casting mold of claim 3, wherein the interlocking feature is a rabbet joint with an interlocking peg adapted to fasten with a second partial ceramic casting mold.
 7. The partial ceramic casting mold of claim 1, wherein the first shell portion comprises a pin support or bumper facing the first core portion.
 8. The partial ceramic casting mold of claim 1, wherein the first core portion comprises a pin support or bumper facing the first core portion.
 9. The partial ceramic casting mold of claim 1, wherein the ceramic mold comprises a plurality of tie structures joining the core portion and shell portion, the tie structures adapted to define a plurality of holes in the cast component upon removal of the mold.
 10. The partial ceramic casting mold of claim 1, wherein the cast component is a turbine blade or a stator vane.
 11. A method for fabricating a partial ceramic mold, comprising: (a) contacting a cured portion of a workpiece with a liquid ceramic photopolymer; (b) irradiating a portion of the liquid ceramic photopolymer adjacent to the cured portion through a window contacting the liquid ceramic photopolymer; (c) removing the workpiece from the uncured liquid ceramic photopolymer; and (d) repeating steps (a)-(c) until a first shell portion of a partial ceramic mold is formed and optionally a first core portion, the optional first core portion and first shell portion adapted to interface with at least an optional second core portion and second shell portion to form a two piece ceramic mold comprising a cavity between the first and/or second core portions and the first and second shell portions, the cavity adapted to define a cast component upon casting and removal of the ceramic mold.
 12. The method of claim 11, wherein the process comprises, after step (d), a step (e) comprising pouring a liquid metal into the two piece ceramic mold and solidifying the liquid metal to form the cast component.
 13. The method of claim 12, wherein the process comprises, after step (e), a step (f) comprising removing the two piece ceramic mold from the cast component.
 14. The method of claim 13, wherein removing the two piece ceramic mold from the cast component comprises a combination of mechanical force and chemical leaching.
 15. The method of claim 11, wherein the first core portion or the first shell portion includes at least one interlocking feature adapted to interface with an interlocking feature on the second core portion or second shell portion.
 16. The method of claim 11, wherein the two piece ceramic mold comprises a plurality of tie structures joining the core portion and shell portion, the tie structures adapted to define a plurality of holes in the cast component upon removal of the two piece ceramic mold.
 17. The method of claim 11, wherein the cast component is a turbine blade or a stator vane.
 18. The method of claim 11, wherein the first shell portion comprises a pin support or bumper facing the first core portion.
 19. The method of claim 11, wherein the first core portion comprises a pin support or bumper facing the first core portion.
 20. The method of claim 11, wherein the first partial ceramic mold has a first core portion and the second partial ceramic mold has a second core portion.
 21. A method of preparing a cast component using the two piece ceramic mold of claim 11 comprising: pouring a liquid metal into the two piece ceramic casting mold and solidifying the liquid metal to form the cast component; and removing the two piece ceramic mold from the cast component.
 22. A method of preparing a cast component comprising: assembling a first core portion and a first shell portion of a two piece ceramic mold with at least a second core portion and second shell portion to form a two piece ceramic mold comprising a cavity between the first and second core portions and the first and second shell portions, the cavity adapted to define the shape of the cast component upon casting and removal of the two piece ceramic mold; pouring a liquid metal into the two piece ceramic casting mold and solidifying the liquid metal to form the cast component; and removing the two piece ceramic casting mold from the cast component. 